- Fiberglass Product
- Texturized Glass Fiber Fabric
- Filament Fiberglass Fabric
- Fiberglass Tape
- Fiberglass Rope
- Fiberglass Sleeve
- Fiberglass Roving/Yarn/Thread
- Fiberglass Mat
- Fiberglass Multiaxial Fabric/Combo Mat
- S-Glass Product
- AR-Glass Product
- Fiberglass Finished Product
- FRP
- Chopped Strand Mat (CSM) & Filament Mat (CFM)
- Electrical Fiberglass Fabric
- Ceramic Fiber Product
- Aramid Fiber Fabric and Textile
- Carbon Fiber Product
- Silica Fabric and Textiles
- Coated Fabric and Textiles
- Aluminium Coated Fiberglass Fabric
- Silicone Coated Fiberglass Fabric
- PTFE Coated Fiberglass Fabric
- PU Coated Fiberglass Fabric
- Acrylic Coated Fiberglass Fabric
- Vermiculite Coated Fiberglass Fabric
- Graphite Coated Fiberglass Fabric
- PVC Coated Fiberglass Fabric
- Calcium Silicate Coated Fiberglass Fabric
- Neoprene Coated Fiberglass Fabric
- EPDM Coated Fiberglass Fabric
- Hypalon Coated Fiberglass Fabric
- Viton Coated Fiberglass Fabric
- SOL Coated Fiberglass Fabric
- Heat Treated Fiberglass Fabric
- Vermiculite Coated Silica Fabric
- Aerogel Product
- Basalt Fiber Product
- Gland Packing and Gasket
- Calcium Silicate Product
- PTFE(Teflon) Product
- Rock Wool & Glass Wool
- Prepreg
- Bio Soluble AES Fiber Product
- Others & Accessories
Basalt Fiber Rebar
Basalt fiber rebar (BFRP) is a new kind of composite material which basalt fiber combines with epoxy resin and curing agent. The difference with steel is that the density of BFRP is 1.9-2.1g/cm3. BFRP is a kind of rust less electrical insulator, with non-magnetic, especially with great acid resistance and alkali resistance. It could develop the durability of construction.
Unitex Basalt fiber rebar is widely used at Earthquake observing station, Seaport pier protection engineering and construction, metro station, bridge, nonmagnetic or magnetic concrete construction, prestressed concrete highway, anti-corrosion chemical industry, Chemical storage tank, underground engineering, Mri (magnetic resonance imaging) facilities basis, Communication building, Electronic equipment factory, Fusion buildings, concrete guide board of Maglev railway, Telecommunications transmission tower, Television stents and strengthen core of optical fiber cable.
1.Nonmagnetic.
2.Electric insulation.
3.High strength, high modulus.
4.Coefficient of thermal expansion near with cement concrete.
5.High resistance to corrosion, chemical, acid, alkali and salt.
6.Not harm to environment and human body.
Code |
BST8100 |
Material: |
Basalt Fiber + Epoxy Resin |
Diameter: |
3mm-40mm |
Density: |
1.9-2.1 g/cm3 |
Tensile Strength |
780-1200 MPa |
E-Modulus: |
58 GPa |
Elongation: |
2.6% |
Magnetic: |
<5×10-7 |
Working Temperature |
-100℃ to 250℃ |
|
-148℉ to 482℉ |
More details and custom size please contact our sales at sales@unitexcomposite.com.