S-Glass Roving
S-Glass Roving is a kind of excellent performance of inorganic non-metallic materials, compared to normal fiberglass, S-glass have 30-40% higher tensile strength, 15-20% higher modulus of elasticity under condition of 4020, 4600MPa, 100-150℃ higher temperature endurance under condition of 82.9, 86.4GPa, 10 times higher fatigue resistance, also they have excellent impact resistance because of high elongation to break, high ageing corrosion resistance, quick resin wet-out properties. Compared to carbon fiber material, S-Glass is non electromagnetic shielding, so it is a good material to produced and used in Military, spacecraft, aerospace, marine bulletproof armor and sports equipment.
Now Unitex provide S-Glass Roving, with USY1, USY2, USY3 three grade, widely used in such as helicopter blades, aircraft flooring and interiors, vehicle and vessel armor protection, fireman and scuba bottles, and high strength timing belts.
Code |
Tex |
Coefficient of Variation (%) |
Moisture content (%) |
Breaking strength (N) |
USY1-240 |
240±7.5% |
≤5 |
≤0.2 |
≥145 |
USY2-240 |
240±7.5% |
≤5 |
≤0.2 |
≥170 |
USY1-480 |
480±7.5% |
≤5 |
≤0.2 |
≥285 |
USY2-480 |
480±7.5% |
≤5 |
≤0.2 |
≥330 |
USY1-660 |
960±5% |
≤5 |
≤0.2 |
≥570 |
USY2-660 |
960±5% |
≤5 |
≤0.2 |
≥670 |
USY1-960 |
960±5% |
≤5 |
≤0.2 |
≥570 |
USY2-960 |
960±5% |
≤5 |
≤0.2 |
≥670 |
USY1-1200 |
1200±5% |
≤5 |
≤0.2 |
≥660 |
USY2-1200 |
1200±5% |
≤5 |
≤0.2 |
≥780 |
USY1-2400 |
2400±5% |
≤5 |
≤0.2 |
≥1200 |
USY2-2400 |
2400±5% |
≤5 |
≤0.2 |
≥1330 |
More details and custom size please contact our sales at sales@unitexcomposite.com.